Ultra Thin Silicone Sheet
Ultra thin silicone rubber film, translucent, (30° shore A hardness).
Offering key pioneering advantages, this new form of presentation greatly extends the reach of high-tech silicone technology. Produced from addition-curing silicone, these films are manufactured under cleanroom conditions to produce flawless, extremely homogeneous films of uniform thickness. Starting at just 20µm (0.02mm), these films are highly elastic, with low modulus, high specific resistivity and high dielectric strength. They are chemically inert and resistant to oxygen, ozone and ultraviolet (UV) radiation whilst being highly permeable to gas and water vapour.
MVQ ultra thin film performs at temperatures of -45°C to +200°C and is an ideal dielectric medium in applications such as actuator technology, generator technology or sensor technology. This film can also be used in food packaging, technical textiles and multiple industrial applications. It can be die-cut or laser cut and bonded with silicone adhesive.
Available as a sheet (250mm x 250mm), or a minimum of 1 meter length.
- Description
- Additional information
- Product Enquiry
Description
ELASTOSIL® Film 2030 250/xxx is a high-precision silicone film made from cross-linked silicone rubber. The film shows a maximum thickness variation across the total width less than ±5%. The precision allows a constant electrical resistance and good comparative tracking resistance across a broad range of temperatures.
The width is 250 mm and thickness is given in μm (xxx). xxx stands for
- 20 µm
- 50 µm
- 100 µm
- 200 µm
- 300 µm
- 400 µm
ELASTOSIL® Film has got the outstanding mechanical and physical properties of platinum cured silicone.
- high and selectively gas and water vapor permeable
- high temperature resistant and low temperature flexible
- high dielectric strength combined with a high specific resistivity
- transparent
- constant mechanical and electrical properties over a wide range of temperatures and operating time
- solvent free
| Property | Condition | Value | Method |
|---|---|---|---|
| Dielectric strength | - | 80 - 100 kV/mm | - |
| Volume resistivity | - | 10¹⁴ Ohmcm | IEC 60093 |
| Hardness Shore A | - | 27° | DIN ISO 48-4 |
| Tensile strength | - | 6.0 N/mm² | ISO 37 type 1 |
| Elongation at break | - | 450 % | ISO 37 type 1 |
| Compression Set | 22 h | 100 °C | 5 % | DIN ISO 815-1 type B method A |
| Gas permeability (selectively) | - | CO₂/N₂ = 10:1 | DIN 53536 |
| Water vapor permeability | 24 h | 20 µm | 3000 g/m² | JIS 1099 A1 |
| Water vapor permeability | 24 h | 50 µm | 1200 g/m² | JIS 1099 A1 |
| Water vapor permeability | 24 h | 100 µm | 800 g/m² | JIS 1099 A1 |
| Glass transition temperature | - | -126 °C | - |
| Operating temperature | - | -45 - 150 °C | - |
| Tear strength | - | 10 N/mm | ASTM D 624 B |
Additional information
| Color | Translucent |
|---|---|
| Thickness | 0.02mm, 0.05mm, 0.1mm, 0.25mm, 0.2mm, 0.3mm, 0.4mm |